| Room-temperature photoluminescence behavior of α-V2O5 and mixed α-β phase V2O5 films grown by electrode position | |||||
| 작성자 | 김** | 작성일 | 2019-07-29 | 조회수 | 121 |
|---|---|---|---|---|---|
|
Journal Article published May 2019 in Materials Science in Semiconductor Processing volume 94 on pages 15 to 21
Research funded by Ministry of EducationMinistry of Education (2009-0093818) | NRFNRF (NRF 2015R1D1A1A0106581)
AbstractVanadium pentoxide (V2O5) films with micro-nanostructure were fabricated by an electrodeposition method using an aqueous solution of NH4VO3. The surface morphology and structural properties of the V2O5 were investigated by SEM and XRD measurements. The results show that the annealing temperature strongly affects the surface morphology, crystal structure, and photoluminescence (PL) properties. The formation of α-V2O5 structure occurred when the sample was annealed at temperatures below 500?℃. As the annealing temperature increases, some of the α-V2O5 structures were distorted and restructured to form a high-quality mix of α-β phase V2O5. This leads to great enhancement of the PL due to the presence of numerous defects on the surface of the V2O5 films. Moreover, the mixing of the α-β phase V2O5 leads to wide absorption and enhancement of the visible-light emission from V2O5 micro-nanostructure. |
|||||